Lithium Aluminum Silicon Ultra-thin Flat Glass for High-end display cover
Lithium Alumino Silicate Glass (CHIYAN-H2) is a newly developed lithium aluminum silicon ultra-thin flat glass for high-end touch displays using float process. Based on the optimized double ion exchange process based on a unique formula, high-pressure stress and deep pressure stress layers are achieved, making the product exhibit extremely strong resistance to falling, punching, scratching and bending strength.
Features:
-
Ultra-high Strengthening Stress can be Achieved
-
Strong Scratch Resistance
-
High Transmittance
-
High Flexibility
-
Excellent Bending Strength Resistance
Application: Widely used in high-end consumer electronics device cover
Regular Thickness:
0.3mm~6mm
CHIYAN-H2’s 0.3~6.0mm thickness Lithium alumino silicate glass has already been used in the market to meet a wide range of customers needs.
Standard Size:1300*1100mm (5th Generation)
Note: The size can be customized according to customer's needs.
Product Composition
Lithium Alumino Silicate Glass achieves better stress and strain depth than ordinary soda-lime glass by increasing the Al₂O₃ content in the glass and increasing the ion exchange capacity.
Physical Property Parameter
| S/N | Items | Unit | CY-H2 |
| 1 | Density | g/cm3 | 2.48 |
| 2 | Refractive Index(590nm) | / | 1.53 |
| 3 | Young's Modulus | Gpa | 84 |
| 4 | Shear Modulus | Gpa | 34 |
| 5 | Volume Resistivity | lg(Ω .cm) | 7.2 |
| 6 | Dielectric Constant | F/m | 6.7 |
| 7 | Softening Point | ℃ | 770 |
| 8 | Strain Point | ℃ | 505 |
| 9 | Annealing Point | ℃ | 550 |
| 10 | Transmittance(0.7mmt,550nm) | % | ≥91 |
| 11 | Thermal Expansivity | * 10-7/℃ | 80 |
| 12 | Photoelastic Coefficient | nm/cm/MPa | 27.4 |
| 13 | Poisson's Coefficient | / | 0.22 |
| 14 | Vickers-hardness(After strengthening) | Kgf/mm² | 685 |
Chemical Tempering Process Parameter
| CS | 700-1000Mpa |
| DOL | 100-160um |
| 4PB | >650Mpa |
Note: Tempering solution Na+<0.5%. The above test results are affected by processing conditions, the data is for reference only, not as a basis for production.
Packaging Diagram
Storage conditions: Temperature ≤30℃, humidity ≤65% (no condensation), shelf life is 6 months from the date of delivery.
Payment Terms: 30% deposit. 70% balance before shipping
Lithium Alumino-Silicate Glass(CHIYAN-H2) is adopted Float Glass Process.
Float glass is made by heating raw materials—silica sand, limestone, soda ash, and magnesium in a furnace. When melted, it’s then spread out over a sizable bed of molten tin. As it moves along rollers in the annealing oven during a controlled cooling process, this mixture slowly solidifies over the molten tin. From this point, a single, continuous smooth ribbon of glass emerges as below picture showed: